SUPER Al-FLO 4047
Complicated aluminum brazing became simply by using this wire. Rest from washing and flushing treatment distress. It is safe for environment too. |
|
- SUPER Al-FLO 4047
|
* |
As non-corrosive flux, which contains cesium, is cored into aluminum wire, this flux cored brazing wire has excellent working property. |
|
|
* |
This flux cored brazing wire is suitable for not only manual brazing but also automatic wire feeding. |
|
|
* |
As the active temperature of flux is low, difficult aluminum brazing operation can be done easily with this flux cored brazing wire. |
|
|
* |
In order to prevent overheating during operation, this flux cored brazing wire wields its power to prevent inferior finish caused by burning.
|
|
|
* |
Compared with old manual flux applying, the suitable and fixed quantity of flux can be applied. Therefore, flux will not be flowed into inside of brazing area. |
|
|
* |
There is no need to apply flux. Moreover, as flux remnants is non-hygroscopic and non-corrosive, cleaning after brazing is not required. |
|
|
* |
As cleaning water drainage treatment is not required, there is no influence on environment contamination. |
|
|
* |
This flux cored brazing wire is suitable for not only manual brazing but also automatic wire feeding. |
|
|
* |
When a customer wants to remove the remained flux due to external appearance, please clean the brazed work piece which is still hot after brazing. Al-FLO flux is easy to remove compared with old nocolok flux. |
- MIG WIRE DIL 350 SPECIFICATION
Brazing Material
(JIS BA 4047) |
Silicon: 11 - 13%, Aluminum: Balance
Melting Temperature: 577°c - 580°c |
Brazing Material
(JIS BA 4047) |
Cesium fluoride, Aluminum fluoride,
Potassium fluoride, Aluminum oxide
Melting Temperature: 510°c |
SUPER Al-FLO 4047
(FLUX CORED WIRE) |
Wire diameter: 1.6ø, 4.5kg/spool reel
Other sizes may be manufactured upon request. |
|
|
|
|